CL-H Crystallit® 2K-PUR is a highly transparent, extremely solid-rich two-pack polyurethane glaze for high-glossy coatings of supplementing porcellain and poros ceramics. It is extremely lightfast.
￼Gloss levels measuring value acc. to DIN 67530 at 60° approx. 92
Curing with PUR-Hardener 5085 in mixing ratio resin / hardener 2:1. The processing time is about 2 hours at RH 20 ° C and 65%. Humidity.
The resin component must be stirred before use. After the mixture of CL-H Crystallit ® and PUR-Hardener 5085 is the resin glaze ready to use and can be applied with a sable brush or airbrush method. Dilution is usually not necessary. The cleaning brushes should be made only with the PU thinner S 9004 and then with acetone.
The prepared, well-cured supplements are administered every 14 hours with a light sanding twice - coated - in rare cases three times.
The original viscosity is approximately 17 s
Shelf life in unopened original container about 1 year
Dry times are at 20 ° C and relative humidity 65%. humidity:
Dust Dry to 30 minutes
to touch 2 hours
sandable approx 14 hrs
Note on the packaging of the glaze hardener:
At the edge of the dosage lid, hardener can escape slightly - this is technically necessary and does not constitute grounds for complaint.
This Product was added to our catalogue on 22/11/2016.